Coldglaze PRO 2 Clear Gloss
SYL-427

Clear
SKU: SYL-427 Category: Tag:

Description

If you are ordering from outside of EUROPE then the products on this page are subject to additional hazardous packing and freight surcharges.

Used on it’s own Coldglaze PRO 2 will replace the glaze effect on china without the use of heat. It has excellent non-yellowing characteristics. It is also mixed with pigments to repaint patterns.

Coldglaze PRO 2 is water resistant, very tough with high strength surface adhesion. It can be airbrushed even when mixed with powder pigments.

Coldglaze PRO 2 can also be mixed with Oil Colours.

Equivalent to Rustins

Equivalent to Tor

FORCE DRYING

To accelerate the drying process, a flash-off period of approximately 10 minutes should be allowed for the solvents to evaporate.

Ceramic & Metal: Temperatures up to 120ºC for 20 – 30 minutes normally recommended

Plastic: Care must be taken to avoid deformation to the plastic. Typically, 60ºC for 2 – 3 hours.

AIR DRYING

Ambient temperature of 20ºC, the drying time is approximately:

Surface Dry
10 -15 Minutes
Hard Dry
2 – 4 Hours
Full Properties
7 Days
Pot Life
7 – 8 Hours

INSTRUCTIONS

  • The mixing ratio is 4 parts resin to 1 part hardener by volume.
  • Thoroughly mix with a small stirrer.
  • pt146 Thinners may be added to thin the mix if required.
  • Apply either by brush or airbrush.
  • If required, add a small amount of pigment until the desired colour.

TO ACHIEVE A MATT FINISH

For a matt finish, simply mix Sylmasta Matting Agent S532 with the Coldglaze PRO 2 to achieve desired finish.

Mix quantities: 70g~80g of Matting Agent per litre of Coldglaze PRO 2.

TO CREATE A WHITE GLAZE

A white glaze can be created in one of two ways:

add 10% Sylmasta CGW White Paste for a high-quality, homogeneous white glaze.

TO AIRBRUSH

To the mixed Coldglaze PRO 2 add approximately 20% by volume of PRO 2 Thinners to obtain a suitable viscosity. Adjustments to the mix can be made, dependent upon desired finish. A wet film thickness of 50 – 60 microns will result in a dry film thickness of 25 microns.